Fabrication and Characterization of Carbon Black and Phenol Formaldehyde Composites

Jakir Hossain, Mohammad Saiful Alam, Shujit Chandra Paul and Shafiul Islam

Carbon black and Phenol formaldehyde composites were prepared by hot press molding at different temperature (180°C, 200°C, 220°C); pressure (100 kN, 150 kN, 200 kN, 250 kN); heating time (10 min, 20 min, 30 min, 60 min) and several compositions (50%C, 60%C, 70%C, 80%C, 90%C). The different properties such as physical, mechanical, thermal properties were studied by Universal Testing Machine (UTM), Micro hardness tester, TGA/DTA analyser and X-Ray diffractometer etc. In this work, it was observed that the bulk density was slightly changed for 50% carbon black and Phenol formaldehyde composites. Compressive strength of sample was increased with increasing the pressure, heating temperature and time.